"Gain and loss of halogen free flame retardant PP"

 1) background

With the progress of society and the accelerating process of industrialization, people also continuously put forward new and higher requirements for the materials. Especially for petroleum chemical industry and coal chemical industry as the main source of polymer materials, not only meet the requirement of material itself the required performance standards, and material preparation and application to comply with the characteristics of resource saving and environment friendly. In recent years, with the development of green chemistry and technology, the halogen-free flame retardant technology has been gradually maturing.

2) halogen-free flame retardant materials

On the basis of green chemistry and technology development of flame retardant materials known as halogen-free flame retardant materials, also known as clean flame retardant materials or ecological material. Narrowly speaking, halogen-free flame retardant materials is refers to the use of halogen-free flame retardant materials. According to the understanding of foreign scholars deeply, halogen free flame retardant technology based on green chemistry and the technology of flame retardant, raw materials selection, flame retardant materials and finished product throughout the design, manufacturing process and waste disposal, etc. The whole ecological chain, and friendly to humans and the environment, as far as possible the use of renewable resources or materials can be recycled, in assuring that there is enough material under the premise of fire safety, with the lowest resource and environmental costs of manufacturing of flame retardant materials.

Second, what is a halogen free? - no halogen industry definition and standard

As is known to all, halogen - antimony flame retardant system with high efficiency and stable flame retardant effect, but its many weaknesses in the worldwide is experiencing a revolution gradually be replaced by:

First plastic material containing halogen in combustion process, generate a lot of poisonous gas on the one hand, on the other hand also generates a lot of thick smoke. According to authoritative statistics, fire deaths more than 80% of smoke and toxic gases from the burning of materials; Second combustion will release hydrogen halide gas, hydrogen halide soluble in water, combined with water vapor in the atmosphere to form acid rain on construction, different degrees of damage crops and human health; Finally, its processing under the condition of heat will release a small amount of hydrogen halide, cause corrosion to the machine or mold.

And industry in general do not restrict the halogen fluorine (F), iodine (I) and astatine (At) the content of halogen free interpretation rules only chloride (Cl) and bromine (Br) two elements in their content and total content of materials or products of limited value. The world is consistent standards organization of halogen free.

Third, the mission of halogen free flame retardant PP - electronic and electrical appliances industry the seeker

Polypropylene (PP) has small density, good rigidity, high strength, chemical resistance and other advantages, and excellent processing performance, is widely used in electronic appliances, household appliances, automobile and other industries.

At the same time, because of PP price is low, the product model, complete modification methods, the most want to achieve general engineering plastics. The flame retardant performance of PP material is an important part of its engineering field, and halogen-free flame retardant PP is in this context came into being, became the electronic and electrical appliances industry seeker!

There is no doubt that gather petrochemical learn halogen-free flame retardant PP (plug smart  5000] become the "leader" of similar products, its products not only functional diversity, performance is complementary, having the general characteristics of halogen free flame retardant PP:

Low smoke, smoke when burning low and does not produce toxic and corrosive gases.

Halogen-free, Cl, Br content of 500 PPM or less, the total content of 1000 PPM or less.

Environmental protection, through the American UL certification, and meet the RoHS and SVHC, PFOS&PFOA, 17 p, PAHs and regulations for the product requirements.

Low density - 20% lower than the same type of halogen flame retardant PP density at least, have a higher cost performance.

And can meet different customer demand for the use of different products, truly for the customer to be tailored, optional DIY service tenet!

Four, gain and loss of halogen free flame retardant PP - swoon

1. The halogen free flame retardant PP flame retardant principle:

Halogen-free flame retardant PP with flame retardant is a kind of expansion type of halogen-free flame retardant, mainly through the condensed phase. At lower temperatures, the flame retardant can produce acid can be used as dehydrating agent; At a slightly higher temperature, acid promote dehydration reaction of PP, and the system in the process of the melt; Dehydration of water vapor and the non-combustible gases produced by PP thermal decomposition has in the molten state of the system expansion foam; Meanwhile, PP ester base in dehydration, carbide form inorganic substances and carbon residue, and the foam system further; Reaction nearing completion, the system of gel and cure, the final formation of porous carbon foam layer.

2. The halogen free flame retardant PP application fields:

Halogen-free flame retardant PP makes material could improve the flame retardancy, and greatly improves the GWIT and GWFI can make it widely used in electronic industry. But flame retardants of halogen free flame retardant PP product ammonium polyphosphate has certain moisture absorption, and ammonium polyphosphate itself has a certain degree of polymerization, its relative PP molecular chain still belong to the category of oligomer.

On the one hand, the crystallization of PP nucleation (including heterogeneous nucleation effect) no promoting effect, on the contrary is similar to the function of the plasticizer;

On the other hand increased the molecular weight distribution of PP, so as to make the neat degree of PP molecular chain to reduce. When our products to gloss, resistance to scraping polishing, voltage more stringent requirements, do not recommend using the product.

Taken the halogen-free flame retardant products applies only to lower parts to gloss requirement;

Taken the PP itself does not scratch resistance, and halogen-free flame retardant antimony series products compared to the same kind of traditional bromine flame retardant and filling systems such as talcum powder and calcium carbonate scratch resistance is relatively weak;

Taken the halogen-free flame retardant PP products suitable for low breakdown voltage requirements of parts, generally not more than 50 kv.

3. The halogen free flame retardant PP common problems and matters needing attention:

(1) after injection molding parts of flame retardant down or not

To end the effect of calcium carbonate, halogen free flame retardant PP series product is sensitive to calcium carbonate, injection can not be mixed with calcium carbonate;

Taken the halogen: the influence of halogen free flame retardant PP series products if mixed with halogen flame retardant products injection molding, will cause the flame retardant efficiency reduce, to a dark appearance, when we do the injection not with halogen flame retardant products;

Taken the carbon black: the influence of halogen free flame retardant PP series product is sensitive to carbon black, if you need to do a film product, advice and professional company, provided by the professional company to do black material or proprietary black masterbatch; The small make up survey, and the petrochemical study this aspect is very strong, might as well go to contact.

Taken the influence of the release agent: because most of the demoulding agent is silicon series of small molecules, the flame retardant efficiency of halogen free flame retardant PP series products have a negative impact, so when we do the injection should be appropriate to reduce the amount of release agent or don't use the release agent;

U back to the influence of materials: due to materials more than certain proportion reduces halogen-free flame retardant PP series products of the flame retardant efficiency, so it should be the proper control and reduce the proportion of the materials back;

Taken the influence of the injection pressure or temperature, injection pressure or temperature is too high, can lead to a halogen free flame retardant PP series products of flame retardant mild decomposition, which reduces the flame retardant efficiency, should be appropriate to reduce injection pressure and injection temperature.

(2) plastic injection parts appear white phenomenon

U die: the influence of halogen free flame retardant PP series products of shrinkage rate is stable, mold choice must be consistent with specific brand shrinkage rate data base;

Taken the influence of the release agent: can be in does not affect the appearance and parts under the premise of flame retardancy appropriate increase the release agent.

Taken the influence of the injection molding process, appropriate to reduce the injection pressure and holding pressure, shorten the holding time, extend the cooling time.

Five, the halogen-free flame retardant in the future

In the future, human will pay more attention to the survival of the environmental problems, halogen free flame retardant technology will play a great role in improving human living environment. No halogenated flame retardant materials is increasingly recognized and attention, people will be on the basis of green industry is environmental friendly product requirements to revise the evaluation methods of flame retardant materials and give unity in the whole world, to a large number of long-term use of flame retardant materials to assess, for flame retardant material in the manufacture, use and recycling and waste treatment each link such as accord with the requirement of environmental protection, harmonious use of flame retardant materials, achieve mutual friendly flame retardant materials and human and society.

Future of halogen free flame retardant technology will be the existing flame retardant technology and nanometer technology, catalytic flame retardant technology, grafted into the combination of new technologies such as carbon flame retardant technology, realize general flame retardant materials, environmental protection, high performance, multiple functional, replace existing some special engineering plastics. It is not only to reduce the cost of flame retardant materials, but also reduce the kinds of plastic material, plastic material recycling and waste treatment focus to bring great convenience